Sintered cermets for tool and wear applications

ABSTRACT

A composition of material comprising aluminum oxide and refractory transition metal diborides, with additions of magnesium oxide and, optionally, transition metal carbides, nitrides, carbonitrides and iron group metals for sintering and grain morphology control, is disclosed, which is particularly useful as a cutting tool for steels, cast iron, and hard to machine materials, such as superalloys. In contrast to the TiC-Al 2  O 3  cermets of the prior art which have to be hot pressed for optimum properties, a large portion of the cermets of the invention can also be fabricated, without detriment to performance, by sintering the cold pressed powder compacts in an inert furnace atmosphere at temperatures between 1650° and 1820° C.

The present invention relates to improved aluminum oxide-based cermets and more particularly to improved cermets based on combinations of aluminum oxide and group IV refractory transition metal diborides. These cermets may also contain further alloying additions consisting of transition metal carbides, nitrides, and carbonitrides, and of iron-group metals. The preferred embodiment of the cermets of the invention is one in which the boride is TiB₂, the alloying additions are TiC, TiN, and Ti(C,N), and to which small amounts of MgO are added to promote sintering.

Commercial ceramic cutting tool materials are available which are based on aluminum oxide, and which usually contains also small additions of MgO or of other metal oxides to promote sintering. In spite of the superior wear resistance of the ceramic cutting tools when compared with conventional cutting tool materials such as carbides, they have gained only limited acceptance because of their low mechanical and thermal shock resistance, and poor fatigue properties.

Alloying additions of metals and carbides (compare the review article on ceramic cutting tool materials by E. D. Whitney, Powder Metallurgical International, Vol. 6, No. 2, 1974, page 73ff) have resulted in considerable improvements, but only through careful control of amount and nature of alloying ingredients and fabrication variables has it become possible to achieve strength and toughness levels at which such cermets become competitive with conventional tool materials in machining certain materials, in particular cast irons. A serious drawback, however, is their high fabrication cost, since hot pressing is required to achieve optimum performance and the desired tool shapes are formed by sectioning of the hot pressed inserts with diamond wheels and subsequent finish-grinding of the cut shapes into the final tool geometry.

In spite of the attractive properties of transition metal borides, among them high hardness and stability, these compounds have found little practical application to date. The difficulty in using these brittle materials is mainly related to their high reactivity, in particular with the iron group metals, which so far has frustrated attempts to develop cemented borides along the same concepts successfully applied to refractory transition metal carbides. Binderless composites based on TiC-TiB₂ (review of related work in R. Kieffer and F. Benesovsky, Hartstoffe und Hartmetalle, Springer, Wien, 1965) and hot pressed TaN-ZrB₂ composites (Y. Murata and E. D. Whitney, Bulletin of the American Ceramic Society, 48, 1969, p. 698) have at times been proposed for cutting tool applications, but their poor strength and fatigue properties have prevented these cermets from gaining commercial importance.

It is accordingly an object of the present invention to provide an improved composition of material based on aluminum oxide and refractory metal diborides, which have improved strength and thermomechanical fatigue characteristics when compared with commercial ceramics and cermets.

It is another object of the present invention to provide an improved composition of material based on aluminum oxide, refractory metal diborides, and refractory metal carbides and carbonitrides, with improved wear resistance and thermomechanical fatigue characteristics when compared with commercial ceramics and cermets.

It is another object of the present invention to provide such oxide-boride compositions which are stable under vacuum sintering conditions and can thus be also fabricated, without detriment to performance, by conventional powder metallurgical techniques.

It is a further object of the present invention to provide cermets based on aluminum oxide and transition metal diborides, which have sufficient strength and thermal deformation resistance, and the necessary chemical characteristics, so as to provide a machine tool which is particularly useful for machining superalloys at high cutting speeds.

Briefly stated, and in accordance with the present invention, a cermet is provided in which the aluminum oxide content is not less than 48 percent by weight of the composition; the refractory metal diboride comprises from 5 to 50 weight percent of the composition and is selected from the group consisting of TiB₂, ZrB₂, and HfB₂ and may also contain up to 20 weight percent of a diboride of a metal selected from the group consisting of vanadium, niobium, tantalum, chromium, molybdenum, and tungsten, the refractory carbide or carbonitride is based on the group IV (titanium, zirconium, and hafnium), group V (vanadium, niobium, and tantalum), and group VI (chromium, molybdenum and tungsten) refractory transition metals, but preferably those of the group IV metals, and may comprise up to 35 weight percent of the composition; the iron group metals can comprise up to 4 weight percent of the composition; and which contains magnesium oxide additions up to 3 percent by weight of the composition to aid in the sintering of the composition.

For a complete understanding of the present invention, together with an appreciation of its other objects and advantages, please see the following detailed description of the attached drawings in which:

FIG. 1 are flank and crater wear curves of an Al₂ O₃ -TiB₂ cermet in machining 4340 steel.

FIG. 2 shows the crater wear of Al₂ O₃ -TiB₂ cermets as a function of the TiB₂ -content in machining 4340 steel.

FIG. 3 shows the average cutting time to edge fracture of Al₂ O₃ -TiB₂ cermets as a function of the TiB₂ content in machining 4340 steel.

FIG. 4 is a wear curve for a cermet composed of 69 wt% Al₂ O₃, 1 wt% MgO, and 30 wt% TiB₂ in machining INCONEL 625.

The ingredients used in the preparation of the cermets of the invention are powders of the oxides and the prealloyed borides, carbides, nitrides, and carbonitrides of the transition metals; the iron group metals are added as elemental powders.

Whatever the manner employed in preparing the composition of the cermet, it is important to select conditions which insure a uniform distribution of the constituents in the alloy blend. This applies in particular to the magnesium oxide, the primary purpose of which is to aid sintering and which is present in only comparatively small quantities in the mixture. A satisfactory distribution of MgO in the alloy blend can be achieved by milling if the grain size of the magnesium oxide ingredient powder is sufficiently small (< 0.2 μ), but preparation of a prehomogenized oxide blend in a separate is recommended if the powder is to coarse. Preparation of such prehomogenized oxide mixtures can be accomplished by different, well-known, methods, such as thermal decomposition of mixtures consisting of hydrated aluminum sulfate and basic magnesium carbonates, or by hydrolysis of the hydrated nitrates of aluminum and magnesium followed by calcination of the product at temperatures slightly above 1000° C. Another method, which results in particularly homogeneous oxide mixtures, consists in evaporating glycol and citric acid complexed solutions of aluminum and magnesium salts, preferably the nitrates, to form a homogeneous, glassy solid, which then is ignited and heated in air to obtain the pure oxide mixture free of organic and inorganic byproducts.

The carbide powders used in the fabrication of the cermets of the invention were commercial products; the nitrides were prepared by direct combination of the elemental metal powders with nitrogen gas at temperatures between 1200° C. and 1700° C., prealloyed carbonitrides of the group IV transition metals were prepared by heating the intimately mixed carbide and nitride ingredient for several hours to temperatures of 2200° C. to 2400° C. under a partial nitrogen atmosphere, while the fabrication procedure for carbonitrides containing group IV and group VI refractory transition metals consisting of nitriding mixtures of group IV metal carbide and group VI metal powders with nitrogen gas at temperatures between 1450° C. and 1650° C. Substoichiometric carbides and nitrides were prepared from the stoichiometric compounds by addition of the required amount of metal powders and homogenization of the mixture at temperatures between 1800° C. and 2100° C. under vacuum (if the alloying ingredients are carbides) or under inert gas (if the alloying ingredients are nitrides).

Aside from the routine fabrication variables, choice of the ingredients and alloying additions and their grain size distributions, as well as milling (mixing) and sintering conditions, strongly influence microstructure and phase constituents and, as a result, the properties of the sintered cermet.

Although no generally valid guidelines can be given because each individual application has its own special requirements and the fabrication method and parameters to be chosen are dependent on the gross composition as well as the compositions and grain size distributions of the individual ingredients, the following observations, which are based on measured property and performance data of the cermets of the invention, may serve as guidelines for characterizing the cermets falling within the scope of the invention.

The best performing cermets are those in which the oxide and the metallic phase form two continuous interpenetrating, lattices, the oxide has a very small grain size, and in which the metallic phase has a dual grain structure, consisting of smaller grains (<1.5μ) and larger grains up to 8 microns in diameter, and constitutes preferably between about 28 and 35 volume percent of the cermet. Among the cermets described in this invention the combinations containing, besides aluminum oxide and magnesium oxide, only the group IV transition metal diborides, in particular TiB₂, have the best sintering properties, are stable under vacuum sintering conditions, and also were found to have the highest bending strength values of any of the cermets studied. However, the oxide-boride composites are also prone to rapid grain growth when heated to more than 50° C. to 70° C. above the normal sintering temperatures of 1725° C. At boride levels less than 30 volume percent, excessive grain coarsing can cause disruption of the three-dimensional continuity of the boride lattice, indicated by the loss of electrical conductivity of the cermet and deterioration of the strength levels to less than 60 thousand pounds per square inch (ksi). Discontinuity of the boride skeleton also results in a relief of the compressive stresses on the aluminum oxide phase, and the characteristic fringe pattern, observed along the aluminum oxide grain boundaries in structures with two interpenetrating skeletons under polarized light, is absent in cermets with isolated diboride grains.

Grain growth stability of the alloy phases is significantly improved by additions of carbides and nitrides, but such additions also necessitate higher sintering temperatures and, generally, an inert gas furnace atmosphere during sintering as such additions can cause undesirable interactions with the aluminum oxide under vacuum at temperatures above 1450° C. to 1500° C. At high concentrations of stoichiometric, or near-stoichiometric, carbides, the pressure-sintering (hot pressing) technique is to be preferred because the lower temperatures required for complete densification aid in diminishing such undesirable interactions between the carbide and the oxide phase.

Lowering of the carbon activity in monocarbides with large homogeneity ranges, such as TiC, by decreasing the carbon content decreases the interaction tendency and also improves the sintering behavior; the properties and performance of such cermets fabricated by cold pressing and sintering under inert gas equaled those fabricated by hot pressing, and generally were superior to tools fabricated from the stoichiometric carbides by either of the two methods. For reasons not yet understood, strength, and performance as tools, of cermets prepared from nitrides with large nitrogen deficiencies were inferior to those fabricated from the stoichiometric or near-stoichiometric compounds.

The following tables and graphs show the performance of a large number of tools having different compositions within the range of the invention, for cermets specially prepared for comparison purposes, and for a prior art Al₂ O₃ -TiC cermet which represents the best of the state of the art ceramic cutting tool materials presently available.

Three different test conditions, one on 4340 steel, one on the superalloy INCONEL 625, and one on the superalloy INCONEL 718, were used. These are designated as Test Condition A, Test Condition B, and Test Condition C. Unless otherwise noted, the test conditions referred to in the tables are as follows:

TEST CONDITION A (Wear and thermomechanical fatigue test)

4340 steel, Rockwell C harness R_(c) 22 to 29; cutting speed 1000 surface feet per minute; feed rate, 0.0152" per revolution; depth of cut, 0.050", no coolant. SNG 433 or SNG 633 inserts, sharp cutting edges.

TEST CONDITION B (Superalloy machinability test)

INCONEL 625, solution-treated R_(c) 29-35; cutting speed, 800 surface feet per minute; feed rate, 0.007" per revolution; depth of cut, 0.100", no coolant. SNG 633 inserts, sharp or lightly honed edges (<0.002" edge radius).

TEST CONDITION C (Superalloy machinability test)

INCONEL 718, solution-treated, R_(c) 27 to 32; cutting speed, 800 surface feet per minute; feed rate, 0.007" per revolution; depth of cut 0.100", no coolant. SNG 433 or SNG 633 inserts, sharp or lightly honed edges (<0.002" edge radius).

The following eight examples which are representative of some of the compositions of the present invention, describe in detail five specific compositions and the manner in which they were fabricated.

EXAMPLE 1

A mixture consisting of 6.400 wt% Al₂ O₃, 1.00 wt% MgO and 35 wt% TiB₂ is thoroughly mixed by ball milling for 30-hours, using naphta or water as milling fluid. The powder slurry is then dried, 6 wt% paraffine added as pressing aid, the mixture homogenized in a blender, and the powder mixture pressed at 3 tones per square inch into parts. The green compacts are packed in aluminum oxide grit, or stacked on graphite plates coated with TiB₂, dewaxed in a 3-hour cycle at 350° C. under vacuum, presintered for 1-hour at 1500° C., and sintered to full density during a 1-hour sintering cycle at 1700° C. to 1730° C. in vacuum. The sintered product had a Rockwell A hardness of R_(A) ˜94, and an average bending strength of 135 ksi.

EXAMPLE 2

The dried powder slurry of the composition described under Example 1 is loaded into graphite dies and hot pressed for 20-minutes at 1600° C. to 1700° C. at a pressure of 3000 psi. The hot pressed part was then shaped into suitable sample geometries by cutting with a diamond wheel. The Rockwell A hardness of the hot pressed cermet was approximately R_(A) ˜94, and the average bending strength 122 ksi.

EXAMPLE 3

A mixture consisting of 63.50 wt% Al₂ O₃, 1.50 wt% MgO, 30 wt% TiB₂, and 5 wt% TiN was processed in the same manner as described under Example 1 and sintered for 1-hour and 30-minutes at 1720° C. under vacuum. The hardness of the sintered cermet was R_(A) ˜93.5 and the average bending strength 110 ksi.

EXAMPLE 4

A mixture consisting of 60 wt% Al₂ O₃, 1.70 wt% MgO, 10 wt% TiB₂ and 28.3 wt% of carbonitride (Ti.sub..83 Mo.sub..17)(C.sub. .86 N.sub..14).sub..91 was processed in the same manner as described under Example 1, the dewaxed compacts presintered for 1-hour at 1450° C. under vacuum, and sintered for 2-hours at 1810° C. to 1830° C. under a furnace gas atmosphere consisting of 99 vol% helium and 1 vol% nitrogen. The hardness of the sintered cermet was R_(A) ˜93 and the average bending strength 113 ksi.

EXAMPLE 5

The dried powder slurry of the composition described under Example 4 was hot pressed for 30-minutes at 1800° C. in graphite dies and the resulting compact sectioned into suitable shapes. The hardness of the hot pressed cermet was R_(A) ˜92, and the average bending strength 123 ksi.

EXAMPLE 6

A mixture consisting of 59.40 wt% Al₂ O₃, 1.60 wt% MgO, 18 wt% TiB₂, and 21 wt% TiC.sub..65 was processed in the same manner as described under Example 1, the dewaxed compacts presintered for 1-hour at 1350° C. under vacuum, and sintered for 2-hours at 1825° C. under helium of ambient pressure. The Rockwell hardness of the sintered cermets was R_(A) ˜93.2, and the average bending strength 126 ksi.

EXAMPLE 7

The dried powder slurry of the composition described under Example 6 was hot pressed for 25-minutes at 1800° C. in graphite and the resulting compact sectioned into suitable shapes. The hardness of the hot pressed cermet was R_(A) ˜94, and the average bending strength 120 ksi.

EXAMPLE 8

A mixture consisting of 43.70 wt% Al₂ O₃, 1.30 wt% MgO, and 55 wt% HfB₂ was processed in the same manner as described under Example 1 and sintered for 1-hour at 1750° C. under vacuum. The sintered cermet had a hardness of R_(A) ˜93 and an average bending strength of 111 ksi.

Test results and performance data for alloy compositions described in these Examples, of other tools in accordance with the invention, and of the prior art Al₂ O₃ -TiC tool when all subject to the test conditions described above, are given in the following Tables 1, 2 and 3, and FIGS. 1, 2, 3 and 4.

FIG. 1 shows the average corner and flank wear and the crater wear as a function of the cutting time of a tool with a gross composition 63.3 wt% Al₂ O₃, 1.7 wt% MgO, and 35 wt% TiB₂ when subjected to Test Condition A.

FIG. 2 shows the average cratering rate of tools prepared from Al₂ O₃ (MgO)-TiB₂ cermets as a function of the TiB₂ content when subjected to Test Condition A.

FIG. 3 shows the average cutting time to edge fracture (fatigue life) of tools prepared from Al₂ O₃ (MgO)-TiB₂ cermets as a function of the TiB₂ content, and also shows the cutting time to edge fracture of the prior art and of a cold pressed and sintered prior art Al₂ O₃ -TiC composite, when subjected to Test Condition A.

                                      Table 1                                      __________________________________________________________________________     Wear Pattern of the Tools Described in Examples 1 through 8 in                 Comparison                                                                     to a Commercial Cermet. Test Condition A.                                      __________________________________________________________________________               Total Cutting                                                                           Notch at                                                                            Corner                                                                              Flank                                                                               Scale                                                                               Crater                                  Tool      Time, Minutes                                                                           Corner                                                                              Wear Wear Line Depth Remarks                           __________________________________________________________________________     Example 1 10.57      -- .008"-                                                                              .009"                                                                               .009"                                                                               .0005"                                                                               --                                "         30.02    <.002"                                                                              .013"                                                                               .015"                                                                               .018"                                                                               .00083"                                                                              --                                Example 2 10.00      -- .009"+                                                                              .010"                                                                               .011"                                                                               .0005"                                                                               --                                "         29.80    chipped                                                                             chipped                                                                             .019"                                                                               .021"                                                                               n.d.  Corner fracture                   Example 3 6.9      chipped                                                                             chipped                                                                             .010"                                                                               .010"                                                                               <.0005"                                                                              "                                 Example 4 7.1      chipped                                                                             chipped                                                                             .008"+                                                                              .009"                                                                               <.0005"                                                                              Corner fracture                   Example 5 10.17      -- .007"                                                                               .007"+                                                                              .008"                                                                               .0045"                                                                               --                                "         14.30    chipped                                                                             chipped                                                                             .009"                                                                               .010"-                                                                              n.d.  Corner fracture                   Example 6 8.10     chipped                                                                             chipped                                                                             .006"                                                                               .008"                                                                               <.0004"                                                                              Corner fracture                   Example 7 10.08      -- .007"                                                                               .007"+                                                                              .008"+                                                                              .0005"                                                                               --                                "         19.60    .003"                                                                               chipped                                                                             .014"                                                                               .017"                                                                               n.d.  Corner fracture                   Example 8 10.36      -- .010"                                                                               .011"                                                                               .013"                                                                               .00055"                                                                              --                                "         17.61    <.002"                                                                              chipped                                                                             chipped                                                                             .019"                                                                               n.d.  Fracture at flank                 Al.sub.2 O.sub.3 -TiC Cermet                                                             10.11      -- .007"-                                                                              .007"+                                                                              .008"                                                                               .0004"                                                                               --                                "         12.32    chipped                                                                             chipped                                                                             .009"                                                                               .010"                                                                               ˜.00055"                                                                       Corner fracture                   __________________________________________________________________________

                                      Table 2                                      __________________________________________________________________________     Wear Pattern of the Tools in Examples 1 through 8 and of other Test            Tools                                                                          in Comparison to a Commercial Cermet. Test Condition B.                        __________________________________________________________________________               Total Cutting                                                                           Notch at                                                                             Corner                                                                             Flank                                                                              Notch at                                                                             Edge  Crater                            Tool      Time, Minutes                                                                           Corner                                                                               Wear                                                                               Wear                                                                               Scale Line                                                                           Wear-back                                                                            Depth    Remarks                  __________________________________________________________________________     Example 1 3.78     .006" .018"                                                                              .036"                                                                              .014" .002" .0021"   --                       Example 2 3.93     .009" .022"                                                                              .044"                                                                              .019" .002" (.002")  --                       Example 3 3.25     .012" .008"                                                                              .016"                                                                              .038" .001" .0017"   --                       Example 4 3.17     .016" .018"                                                                              .023"                                                                              .050" .001" .0015"   --                       Example 5 3.63     .010" .009"                                                                              .016"                                                                              .026" .0015"                                                                               .002"    --                       Example 6 3.34     .010" .012"                                                                              .022"                                                                              .032" .002" (.002")  --                       Example 7 4.01     .008" .021"                                                                              .032"                                                                              .042" .002" .0022"   --                       Example 8 3.43     .016" chip                                                                           .024"                                                                              .044"                                                                              .016" .0022"                                                                               .002"    --                       Tool A    4.33     .008" .011"                                                                              .016"                                                                              .031" .0027"                                                                               (.0027") --                       Tool B    4.16     .006" .020"                                                                              .040"                                                                              .036" .0025"                                                                               (.0025") --                       Tool C    4.47     .006" .022"                                                                              .036"                                                                              .024" .002" (.002")  --                       Al.sub.2 O.sub.3 -TiC Cermet                                                             1.41     .006" .004"                                                                              .012"                                                                              .016"  --   .0008"   Crack at scale                                                                 line                     "         1.43     .006" chipped        --   --       Flank broke              __________________________________________________________________________                                                           down                      Tool A: Example 3, pressure-sintered                                           Tool B: 69 Al.sub.2 O.sub.3, 1.0 MgO, 30 TiB.sub.2, vacuum-sintered            Tool C: 72 Al.sub.2 O.sub.3, MgO, 27 TiB.sub.2, vacuum-sintered          

                                      Table 3                                      __________________________________________________________________________     Wear Pattern of the Tools in Examples 1 through 8. Test Condition              __________________________________________________________________________           Total Cutting                                                                           Notch at                                                                              Corner                                                                              Flank                                                                               Notch at                                                                             Edge  Crater                             Tool  Time, Minutes                                                                           Corner Wear Wear Scale Line                                                                           Wear-back                                                                            Depth                                                                               Remarks                       __________________________________________________________________________     Example 1                                                                            3.46     .012"  .010"                                                                               .016"                                                                               .013" --    <.001                                                                               Uneven edge wear              Example 3                                                                            3.25     .020" chip                                                                            .008"                                                                               .016"                                                                               .075" --    <.001                                                                               "                             Example 5                                                                            2.86     .012"  .012"                                                                               .010"                                                                               .060" --    <.001                                                                               Rough wearland at                                                              corner                        Example 7                                                                            2.35     .050"  .010"                                                                               .010"                                                                               .042" --    <.001                                                                               Severe notching at            __________________________________________________________________________                                                      corner                   

FIG. 4 shows the averaged crater and flank wear of a tool with a gross composition of 69 wt% Al₂ O₃, 1 wt% MgO, and 30 wt% TiB₂ as a function of the cutting time in machining INCONEL 625 under the following conditions: Cutting speed, 1000 surface feet per minute; feed rate, 0.0051" per revolution; depth of cut, 0.100"; no coolant. Tool geometry SNG 433, sharp edges.

It is seen from the curves of FIGS. 3 through 6 and Tables 1 through 3 that the tools within the range of the present invention have superior fatigue life in machining steels when compared to ceramic tools designed for similar applications, the cratering rates are about equal to those measured for the commercial tool, while the flank wear rates, in the average, are slightly higher during the wear-in period of the tools. The good performance on the superalloys at high metal removal rates, and without coolant, is indicative of the high edge strength and thermal deformation resistance of the cermets of the invention. It is further thought that boric acid, formed by surface oxidation of the boride component in the cermet during the machining operation, serves as a lubricant between tool and workpiece and therefore is a contributing factor in the good performance of these tool materials in machining the superalloys at high cutting speeds.

The following Tables 4 and 5 contain test data for a number of tools prepared from specific compositions in accordance with the present invention when subjected to Test Condition A. When examining the data it will be appreciated that many of the alloys listed in Tables 4 and 5, even when fabricated under optimum conditions, are outside the composition ranges considered competitive with existing tool materials in the envisioned area of application, but have been included to outline more clearly the useful composition boundaries of the alloys of the invention. Table 6 contains test data from tools fabricated from boride-free composites for composition purposes, when subjected to Test Condition A.

                                      Table 4.                                     __________________________________________________________________________     Selected List of Oxide-Boride Cermets (Tool Life Data for Test Condition       A)                                                                             __________________________________________________________________________                                 Average Cutting                                    Gross Composition    Fabrication                                                                           Time to Edge                                       of Cermet, wt. %     Method(*)                                                                             Fracture, Minutes                                                                         Remarks                                 __________________________________________________________________________     84.5 Al.sub.2 O.sub.3, 0.5 MgO, 15 TiB.sub.2                                                        Vac    4.6        trace-porosity                          "                    PS     4.3        coarse TiB.sub.2                        "                    Gas    2.3        light porosity, coarse                  84.0 Al.sub.2 O.sub.3, 1.00 MgO, 15 TiB.sub.2                                                       Vac    6.0        --                                      "                    PS     6.0        --                                      "                    Gas    4.6        trace porosity                          83.5 Al.sub.2 O.sub.3, 1.5 MgO, 15TiB.sub.2                                                         Vac    7.3        --                                      "                    PS     6.6        --                                      "                    Gas    4.2        --                                      79.5 Al.sub.2 O.sub.3, 0.5 MgO, 20 TiB.sub.2                                                        Vac    6.6        --                                      "                    PS     5.0        coarse grain                            "                    Gas    2.4        "                                       79.0 Al.sub.2 O.sub.3, 1.0 MgO, 20 TiB.sub.2                                                        Vac    9.5        --                                      "                    PS     9.0        --                                      "                    Gas    6.6        --                                      78.5 Al.sub.2 O.sub.3, 1.5 MgO, 20 TiB.sub.2                                                        Vac    9.3        --                                      "                    PS     10.0       --                                      "                    Gas    5.6        coarse grain                            78.0 Al.sub.2 O.sub.3, 2.0 MgO, 20 TiB.sub.2                                                        Vac    8.0        --                                      "                    PS     7.0        --                                      "                    Gas    4.3        coarse grain                            74.5 Al.sub.2 O.sub.3, 0.5 MgO, 25 TiB.sub.2                                                        Vac    7.5        --                                      "                    PS     6.2        coarse grain                            "                    Gas    6.6        coarse grain                            69.5 Al.sub.2 O.sub.3, 0.5 MgO, 30 TiB.sub.2                                                        Vac    14         --                                      "                    PS     17         --                                      "                    Gas    9          slight porosity                         69.0 Al.sub.2 O.sub.3, 1.0 MgO, 30 TiB.sub.2                                                        Vac    22         --                                      "                    PS     14         coarser grain                           "                    Gas    12         --                                      68.5 Al.sub.2 O.sub.3, 1.5 MgO, 30 TiB.sub.2                                                        Vac    26         --                                      "                    PS     16         coarser grain                           "                    Gas    19         --                                      68.0 Al.sub.2 O.sub.3, 20 MgO, 30 TiB.sub.2                                                         Vac    18         --                                      "                    PS     15         --                                      "                    Gas    19         --                                      67.0 Al.sub.2 O.sub.3, 3.0 MgO, 30 TiB.sub.2                                                        Vac    18         --                                      "                    PS     14         --                                      "                    Gas    16         --                                      65.0 Al.sub.2 O.sub. 3, 5.0 MgO, 30 TiB.sub.2                                                       Vac    13         --                                      "                    PS     8.8        --                                      "                    Gas    11         --                                      65.0 Al.sub.2 O.sub.3, 5.0 TiO, 30 TiB.sub.2                                                        Vac    not tested porosity                                "                    PS     5.6        --                                      "                    Gas    not tested porosity                                65.5 Al.sub.2 O.sub.3, 0.5 MgO, 35 TiB.sub.2                                                        Vac    11         light porosity                          "                    PS     31         --                                      "                    Gas    9.6        light porosity                          64.0 Al.sub.2 O.sub.3, 1.0 MgO, 35 TiB.sub.2                                                        Vac    >30        not tested to destruction               "                    PS     30         --                                      "                    Gas    16         coarse grain                            63.5 Al.sub.2 O.sub.3, 1.5 MgO, 35 TiB.sub.2                                                        Vac    48         --                                      "                    PS     34         --                                      "                    Gas    11         Coarse grain                            63.0 Al.sub.2 O.sub.3, 2.0 MgO, 35 TiB.sub.2                                                        Vac    35         --                                      "                    PS     41         --                                      "                    Gas    14         coarse grain                            61.5 Al.sub.2 O.sub.3, 0.5 MgO, 38 TiB.sub.2                                                        Vac    46         not tested to destruction               "                    PS     6          light porosity                          61.0 Al.sub.2 O.sub.3, 1.0 MgO, 38 TiB.sub.2                                                        Vac    43         --                                      "                    PS     18         coarse grain                            60.5 Al.sub.2 O.sub.3, 1.5 MgO, 38 TiB.sub.2                                                        Vac    35         --                                      "                    PS     29         --                                      60.0 Al.sub.2 O.sub.3, 2 MgO, 38 TiB.sub.2                                                          Vac    33         --                                      "                    PS     36         --                                      66.5 Al.sub.2 O.sub.3, 0.5 MgO, 43 TiB.sub.2                                                        Vac    26         --                                      "                    PS     26         --                                      66.0 Al.sub.2 O.sub.3, 1.0 MgO, 43 TiB.sub.2                                                        Vac    29         --                                      "                    PS     26         --                                      65.5 Al.sub.2 O.sub.3, 1.5 MgO, 43 TiB.sub.2                                                        Vac    37         --                                      "                    PS     16         coarse grain                            49.5 Al.sub.2 O.sub.3, 0.5 MgO, 50 TiB.sub.2                                                        Vac    19         --                                      49.0 MgO, 1.0 MgO, 50 TiB.sub.2                                                                     Vac    26         --                                      "                    PS     19         --                                      48.5 MgO, 1.5 MgO, 50 TiB.sub.2                                                                     Vac    23         --                                      39.5 Al.sub.2 O.sub.3, 0.5 MgO, 60 TiB.sub.2                                                        Vac    8.6        --                                      39.0 Al.sub.2 O.sub.3, 1.0 MgO, 60 TiB.sub.2                                                        Vac    4.9        --                                      24.5 Al.sub.2 O.sub.3, 0.5 MgO, 75 TiB.sub.2                                                        Vac    2.9        --                                      "                    PS     1.4        light porosity                          24 Al.sub.2 O.sub.3, 1.0 MgO, 75 TiB.sub.2                                                          Vac    3.6        --                                      "                    PS     1.9        trace porosity                          65.0 Al.sub.2 O.sub.3, 1.0 MgO, 34 ZrB.sub.2                                                        Vac    9.4        --                                      "                    PS     4.6        porosity                                64.5 Al.sub.2 O.sub.3, 1.5 MgO, 34 ZrB.sub.2                                                        Vac    8.4        --                                      "                    PS     3.6        trace porosity                          51.0 Al.sub.2 O.sub.3, 1.0 MgO, 48 HfB.sub.2                                                        Vac    12         --                                      "                    PS     13         --                                      39.5 Al.sub.2 O.sub.3, 0.5 MgO, 60 HfB.sub.2                                                        Vac    21         --                                      "                    PS     16         --                                      63.5 Al.sub.2 O.sub.3, 1.5 MgO, 35 VB.sub.2                                                         Vac    1.4        porous                                  "                    PS     6.6        --                                      55.7 Al.sub.2 O.sub.3, 1.3 MgO, 43 VB.sub.2                                                         Vac    1.9        porous                                  59.0 Al.sub.2 O.sub.3, 1.0 MgO, 40 NbB.sub.2                                                        Vac    3.2        light porosity                          58.5 Al.sub.2 O.sub.3, 1.5 MgO, 40 NbB.sub.2                                                        Vac    2.6        light porosity, coarse grain            49.0 Al.sub.2 O.sub.3, 1.0 MgO, 50 NbB.sub.2                                                        Vac    1.4        light porosity, coarse grain            48.5 Al.sub.2 O.sub.3, 1.5 MgO, 50 NbB.sub. 2                                                       Vac    not tested very porous                             44.0 Al.sub.2 O.sub.3, 1.0 MgO, 55 TaB.sub.2                                                        Vac    3.2        coarse grain                            34.0 Al.sub.2 O.sub.3, 1.0 MgO, 65 TaB.sub. 2                                                       Vac    1.4        porous, coarse grain                    "                    PS     6.4        --                                      64.0 Al.sub.2 O.sub.3, 1.0 MgO, 35 CrB.sub.2                                                        Vac    not tested very porous                             "                    PS     5.8        --                                      54.0 Al.sub.2 O.sub.3, 1.0 MgO, 45 CrB.sub.2                                                        Vac    not tested very porous                             "                    PS     4.2        --                                      44.0 Al.sub.2 O.sub.3, 1.0 MgO, 55 MoB.sub.2                                                        Vac    1.9        porous                                  "                    PS     3.8        --                                      50.0 Al.sub.2 O.sub.3, 1.0 MgO, 25 TiB.sub.2, 24 HfB.sub.2                                          Vac    23         --                                      64.0 Al.sub.2 O.sub.3, 1.0 MgO, 25 TiB.sub.2, 10 CrB.sub.2                                          PS     21         --                                      60.0 Al.sub.2 O.sub.3, 1.0 MgO, 25 TiB.sub.2, 14 ZrB.sub.2                                          Vac    18         --                                      64.0 Al.sub.2 O.sub.3, 1.0 MgO, 25 TiB.sub.2, 10 VB.sub.2                                           PS     19         --                                      44.0 Al.sub.2 O.sub.3, 1.0 MgO, 40 HfB.sub.2, 15 CrB.sub.2                                          Vac    not tested porous                                  "                    PS     22         --                                      44.0 Al.sub.2 O.sub.3, 1.0 MgO, 42 HfB.sub.2, 13 NbB.sub.2                                          Vac    4.4        porous                                  "                    PS     17         --                                      __________________________________________________________________________      (*)Vac = Vacuum sintered, 1650° to 1730° C                       PS = Pressure sintered, 1600° to 1780° C                         Gas = Sintered under a noble gas atmosphere of ambient pressure          

                                      Table 5.                                     __________________________________________________________________________     Selected List of Oxide-Boride Cermets with Alloying Additions                  (Tool Life Data for Test Condition A)                                          __________________________________________________________________________                                          Average Cutting                           Gross Composition of          Fabrication                                                                           Time to Edge                              Cermet, wt.%                  Method(*)                                                                             Fracture, Minutes                                                                         Remarks                        __________________________________________________________________________     64.0 Al.sub.2 O.sub.3, 1.0 MgO, 30 TiB.sub.2, 5 TiN                                                          Vac    6.9        light porosity                 "                             PS     27         --                             "                             Gas    21         --                             64.0 Al.sub.2 O.sub.3, 1.0 MgO, 25 TiB.sub.2, 10 TiN.sub..67                                                 Vac    5.6        --                             "                             PS     7.3        --                             "                             Gas    6.9        --                             62.4 Al.sub.2 O.sub.3, 1.6 MgO, 18 TiB.sub.2, 18 TiN                                                         Vac    3.2        light porosity                 "                             Gas    8.9        --                             59.5 Al.sub.2 O.sub.3, 0.5 MgO, 10 TiB.sub.2, 30 TiN                                                         Vac    4.4        --                             "                             Gas    8.2        --                             59.5 Al.sub.2 O.sub.3, 0.5 MgO, 29 TiB.sub.2, 11 TiN                                                         Vac    2.2        light porosity                 "                             Gas    2.9        light porosity                 50 Al.sub.2 O.sub.3, 1.50 MgO, 24.25 TiB.sub.2, 24.25 Ti(N.sub..5              N.sub..5)                     Gas    6.6        high surface porosity          "                             PS     9.6        --                             62.5 Al.sub.2 O.sub.3, 1.5 MgO, 18 TiB.sub.2, 18 Ti (C.sub..5 N.sub..5).su     b..8                          Gas    4.3        high surface porosity          "                             PS     11         --                             64.0 Al.sub.2 O.sub.3, 1.0 MgO, 30 TiB.sub.2, 5 TiC.sub..55                                                  Vac    8.7        trace porosity                 "                             PS     32         --                             "                             Gas    28         --                             64.0 Al.sub.2 O.sub.3, 1.0 MgO, 25 TiB.sub.2, 10 TiC.sub..92                                                 Vac    <.1        very porous                    "                             PS     24         --                             "                             Gas    27         --                             64.0 Al.sub.2 O.sub.3, 1.0 MgO, 20 TiB.sub.2, 15 TiC.sub..90                                                 Vac    <.1        very porous                    "                             PS     22         --                             "                             Gas    20         --                             64.0 Al.sub.2 O.sub.3, 1.0 MgO, 10 TiB.sub.2, 35 TiC                                                         Gas    3.9        light porosity                 "                             PS     7          --                             59.5 Al.sub.2 O.sub.3, 0.5 MgO, 29 TiB.sub.2, 11 TiC                                                         Gas    16         --                             "                             PS     6          coarse grain                   60.7 Al.sub.2 O.sub.3, 1.3 MgO, 24 TiB.sub.2, 14 (Ti.sub..83 Mo.sub..17)(C     .sub..86 N.sub..14).sub..91   Gas    23         --                             "                             PS     5.5        coarse grain                   40.0 Al.sub.2 O.sub.3, 1 MgO, 49 HfB.sub.2, 11 TiN                                                           Vac    6.9        --                             "                             PS     17         --                             "                             Gas    19         --                             40 Al.sub.2 O.sub.3, 1 MgO, 49 HfB.sub.2, 11 TiC.sub..92                                                     Gas    <.3        porous                         "                             PS     16         --                             62.5 Al.sub.2 O.sub.3, 30 TiB.sub.2, 6 Ni, 1.5 Mo                                                            Vac    17         final failure by wear          57.5 Al.sub.2 O.sub.3, 20 TiB.sub.2, 6 Ni, 15 TiN, 1.5 Mo                                                    Vac    7.9        light porosity                 "                             Gas    6.1        "                              57.5 Al.sub.2 O.sub.3, 20 TiB.sub.2, 6 Ni, 15 TiC, 1.5 Mo                                                    Vac    14         --                             "                             Gas    3          light porosity                 63 Al.sub.2 O.sub.3, 33 TiB.sub.2, 4 Fe                                                                      Vac    19         final failure by wear          "                             Gas    6.9        light porosity                 62 Al.sub.2 O.sub.3, 32 TiB.sub.2, 6 WC                                                                      Vac    21         --                             "                             Gas    9          coarse grain                   __________________________________________________________________________      (*)Legend, see Table                                                     

                                      Table 6                                      __________________________________________________________________________     Selected List of Boride-free Cermets Fabricated for Comparison Purposes        (Tool Life Data for Test Condition A).                                         __________________________________________________________________________                                         Average Cutting                            Gross Composition of         Fabrication                                                                           Time to Edge                               Cermet, wt.%                 Method(*)                                                                             Fracture, Minutes                                                                         Remarks                         __________________________________________________________________________     78.5 Al.sub.2 O.sub.3, 1.5 MgO, 20 TiC                                                                      Gas    5.8        --                              "                            PS     7.6        --                              64.0 Al.sub.2 O.sub.3, 0.5 MgO, 35.5 TiC                                                                    Gas    4.6        light porosity                  "                            PS     10.6       --                              64.0 Al.sub.2 O.sub.3, 1.0 MgO, 35 TiC.sub..92                                                              Gas    10.2       --                              "                            PS     11.2       --                              63.5 Al.sub.2 O.sub.3, 1.5 MgO, 35 TiC                                                                      Gas    8.1        --                              "                            PS     10.8       --                              59.5 Al.sub.2 O.sub.3, O.5 MgO, 40 TiC                                                                      Gas    4.4        light porosity                  "                            PS     8.6        --                              58.5 Al.sub.2 O.sub.3, 1.5 MgO, 40 TiC                                                                      Gas    9.1        --                              "                            PS     6.4        coarse grain                    63.0 Al.sub.2 O.sub.3, 1.7 MgO, 35.3 TiN                                                                    Vac    5.4        --                              "                            PS     9.4        --                              "                            Gas    8.9        --                              50.0 Al.sub.2 O.sub.3 , 1.5 MgO, 48.5 TiN                                                                   Vac    not tested --                              "                            PS     7.6        --                              "                            Gas    6.3        --                              68.7 Al.sub.2 O.sub.3, 30.3 TiN                                                                             PS     14         edge chamfered                  66.2 Al.sub.2 O.sub.3, 2 Ni, 0.5 Mo, 30.3 TiN                                                               PS     not tested porous, coarse grain            70 Al.sub.2 O.sub.3, 30 Ti(C.sub..5 N.sub..5)                                                               PS     9.9        --                              63.5 Al.sub.2 O.sub.3, 2 Ni, 0.5 Mo, 34(Ti.sub..83 Mo.sub..17)(C.sub..86       N.sub..14).sub..9            PS     .9         porous                          60 Al.sub.2 O.sub.3, 1.5 MgO, 38.5 (Ti.sub..83 Mo.sub..17)(C.sub..86           N.sub..14).sub..91           Gas    13.2       --                              "                            PS     6.7        coarse grain                    50 Al.sub.2 O.sub.3, 1.5 MgO, 48.5 (Ti.sub..83 Mo.sub..17)(C.sub..86           N.sub..14).sub..91           Gas    10.1       --                              "                            PS     8.6        --                              60 Al.sub.2 O.sub.3,1.5 MgO, 38.5 (Ti.sub..75 Mo.sub..25)(C.sub..80            N.sub..20).sub..90           Gas    6.2        --                              "                            PS     10.2       --                              60 Al.sub.2 O.sub.3, 1.5 MgO, 38.5 (Ti.sub..7 Mo.sub..3)(C.sub..82             N.sub..18).sub..85           Gas    1.9        --                              "                            PS     3.6        --                              63.5 Al.sub.2 O.sub.3, 1.5 MgO, 35 (Ti.sub..8 Mo.sub..1 Cr.sub..1)(C.sub..     8 N.sub..2)                  Gas    8.0        --                              "                            PS     4.1        coarse grain                    68 Al.sub.2 O.sub.3, 32 Ti(N.sub..75 O.sub..25)                                                             PS     2          fine cracks throughout                                                         tool                            68 Al.sub.2 O.sub.3, 32 Ti(C.sub..75 O.sub..25)                                                             PS     2          "                               45 Al.sub.2 O.sub.3, 0.5 MgO, 54.5 HfC                                                                      PS     7.5        --                              44.5 Al.sub.2 O.sub.3, 0.5 MgO, 55 HfN                                                                      PS     not tested porous                          46.5 Al.sub.2 O.sub.3, 0.5 MgO, 53 Hf (C.sub..5 N.sub..5)                                                   PS     4          --                              54.5 Al.sub.2 O.sub.3, 0.5 MgO, 45 (Hf.sub..75 Ti.sub..25)(N.sub..75           O.sub..25)                   PS     not tested fine cracks throughout                                                         tool                            60 Al.sub.2 O.sub.3, 40 ZrN  PS     4.4        --                              60 Al.sub.2 O.sub.3, 40 (Zr.sub..75 Ti.sub..25)(N.sub..75 O.sub..25)                                        PS     9.1        --                              64 Al.sub.2 O.sub.3, 36 (Ti.sub..5 Nb.sub..5)N                                                              PS     11         --                              65 Al.sub.2 O.sub.3 , 35 (Ti.sub..5 V.sub..5)N                                                              PS     6.8        --                              67 Al.sub.2 O.sub.3, 33 (Ti.sub..75 Nb.sub..25)(N.sub..75 O.sub..25)                                        PS     10.5       --                              65 Al.sub.2 O.sub.3, 0.5 MgO, 34.5 (Ti.sub..82 Cr.sub..18)(C.sub..82           N.sub..18)                   PS     7.5        --                              65 Al.sub.2 O.sub.3, 35 (Ti.sub..78 Cr.sub..22)(C.sub..78 N.sub..22)                                        PS     5.5        --                              65 Al.sub.2 O.sub.3, 35 (Ti.sub..65 Cr.sub..35)(C.sub..65 N.sub..35)                                        PS     5.0        --                              50 Al.sub.2 O.sub.3, 50 (Ti.sub..78 Cr.sub..22)(C.sub..78 N.sub..22)                                        PS     7.0        --                              29 Al.sub.2 O.sub.3, 71 (Ti.sub..78 Cr.sub..22)(C.sub..78 N.sub..22)                                        PS     6.6        --                              80 TiC, 20 TiB.sub.2         Gas    1.6        breakdown at scale line         80 TiN, 20 TiB.sub.2         Gas    2.3        "                               Commercial Al.sub.2 O.sub.3 -TiC Cermet                                                                     (PS)   12         chamfered edges reground                                                       to                                                                             sharp edges                     __________________________________________________________________________      (*) For legend, see Table                                                

The following paragraphs summarize the effects of different alloying additions on fabricability, properties, and performance of the cermets of the invention.

1. Additions of MgO improve sinterability of the compositions of the invention, but high levels tend to increase the notching tendency of the tools. The optimum concentrations of MgO are approximately 0.2 to 0.6 percent by weight of the amount of Al₂ O₃ for cermets to be fabricated by pressure-sintering, and between 1 and 2 wt% of the amount of alumina for materials prepared by cold pressing and sintering.

2. Wear and cratering resistance of the tools decrease with increasing boride content. Cermets containing the group IV refractory transition metal borides show the best performance, although the presence of smaller amounts, generally less than 20% of the weight of the group IV metal diboride, of other refractory transition metal diborides can be tolerated without significant changes in performance. Use of borides containing only group V and group VI metal as boride component in the alloy formulations is not recommended, because of poor sintering and strength properties of such compositions. Vaporization of the metal component of cermets containing high concentrations of VB₂ and CrB₂ during vacuum sintering usually results in high porosity and such compositions are therefore preferably fabricated by pressure-sintering.

3. Additions of carbides, nitrides, and carbonitrides, have a very pronounced effect on grain growth stability of the alloys but increase the sintering temperatures required for complete densification and, particularly in the case of carbides, require use of an inert gas sintering atmosphere. Among the available transition metal compounds, the carbides, carbonitrides, and nitrides of the group IV transition metals, which may be alloyed with smaller amounts of group V and group VI transition metals, are the preferred choice. Cermets containing substantial amounts of ZrN and HfN are difficult to sinter to full density and are therefore preferably fabricated by pressure-sintering.

4. Addition of smaller amounts (<4 wt%) of ferrous metals, optionally alloyed with smaller amounts of refractory transition metals such as molybdenum, tungsten and chromium, permit a 50° C. to 75° C. lowering of the sintering temperature of boride-containing cermets. Tools prepared from ferrous metal-alloyed cermets show good fatigue life but are less wear resistant than the iron metal free grades.

Additions of ferrous metals to cermet compositions which contain a high proportion of carbides, nitrides, or carbonitrides, are only possible if the compositions are to be sintered under pressure; when heating cold pressed parts of such compositions to sintering temperature, the ferrous alloy tends to migrate to the part surfaces, with the interiors of the sintered parts remaining porous.

5. Composite tools consisting of a laminate of a tough carbide substrate and a thin layer (<0.7 mm) of a cermet can be used with advantage to decrease gross fracture sensitivity of the cermets in machining applications. A suitable procedure for forming the composite tool consists of electroplating a thin as-sintered, or preground, cermet plate with nickel and brazing the coated plate to the carbide substrate with a Cu-Ni-Ti alloy. Wear performance of composite tools prepared in this manner were found to be equivalent to that of solid cermet tools.

The data shown in the above Tables and graphs are representative of many other alloys within the range of the invention which were prepared and tested. It becomes evident from a comparison of the performance data that the new compositions of the present invention offer a substantial improvement in overall performance of the state of the art tools in machining steels and are particularly useful for machining superalloys at high metal removal rates.

While the invention is thus disclosed and many embodiments described in detail, it is not intended that the invention be limited to those shown embodiments. Instead, many embodiments and uses will occur to those skilled in the art which fall within the spirit and scope of the invention. It is intended that the invention be limited only by the appended claims. 

What is claimed is:
 1. A composition of material consisting essentially of aluminum oxide, magnesium oxide, refractory transition metal diborides, refractory transition metal carbides and nitrides and alloying metals selected from the group consisting of the iron metals, chromium, molybdenum and tungsten, in which the aluminum oxide comprises at least 48 weight percent of the composition, the refractory transition metal diborides comprise from 5 to 50 weight percent of the composition, the refractory transition metal carbides and nitrides comprise from 0 to 35 weight percent of the composition, in which said magnesium oxide comprises between 0.3 and 3 weight percent of the composition and the alloying metals comprise from 0 to 6 weight percent of the composition.
 2. A composition of material according to claim 1 which is a sintered material with the aluminum oxide and the additional components combined forming two separate, but each continuous interpenetrating skeletons in the sintered structure.
 3. A composition of material according to claim 1 in which the refractory transition metal diborides are diborides of a metal selected from the group consisting of titanium, zirconium and hafnium.
 4. A composition of material according to claim 1 in which the refractory metal carbides and nitrides are carbides and nitrides of metals selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten.
 5. A composition of material according to claim 1 in which the transition metal diborides contain up to 20 weight percent of a diboride of a metal selected from the group consisting of vanadium, niobium, tantalum, chromium, molybdenum, and tungsten, with the balance of the transition metal diboride being a diboride of metal selected from the group consisting of titanium, zirconium and hafnium.
 6. The method of forming a composition of material according to claim 1, comprising the steps of:preparing a mixture of alloy ingredients under inert fluids or gases, until it has uniform consistency and the desired grain size distribution; compacting the mixture into a desired shape; and sintering the compacts so formed at temperatures between 1650° C and 1830° C under vacuum or an inert gas atmosphere.
 7. The method of forming a composition of material according to claim 1, comprising the steps of:preparing a mixture of alloy ingredients under inert fluid and gases, until it has uniform consistency and the desired grain size distribution; pressure-sintering the mixture for 15 to 60 minutes at temperatures between 1650° C and 1830° C; and shaping the thus formed compact by cutting to the desired shape and size.
 8. The method of claim 6 which further comprises the step of affixing a thin plate of the sintered compact to a carbide cutting tool so as to form a composite cutting tool.
 9. The method of claim 7 which further comprises the step of affixing a thin plate of the sintered compact to a carbide cutting tool so as to form a composite cutting tool. 